ASTM A537/A537M-13(2019)

Standard Specification for Pressure Vessel Plates, Heat-Treated, Carbon-Manganese-Silicon Steel

Soveltamisala
1.1 This specification2 covers heat-treated carbon-manganese-silicon steel plates intended for fusion welded pressure vessels and structures. 1.2 Plates furnished under this specification are available in the following three classes:  Class  Heat Treatment  Thickness Yield Strength, min, ksi [MPa] Tensile Strength, min, ksi [MPa] 1 Normalized 21/2 in. and under [65 mm and under] 50 [345] 70 [485] Over 21/2 to 4 in. [Over 65 to 100 mm] 45 [310] 65 [450] 2 Quenched and tempered 21/2 in. and under [65 mm and under] 60 [415] 80 [550] Over 21/2 to 4 in. [Over 65 to 100 mm] 55 [380] 75 [515] Over 4 to 6 in. [Over 100 to 150 mm] 46 [315] 70 [485] 3 Quenched and tempered 21/2 in. and under [65 mm and under] 55 [380] 80 [550]     Over 21/2 to 4 in. [Over 65 to 100 mm] 50 [345] 75 [515]     Over 4 to 6 in. [Over 100 to 150 mm] 40 [275] 70 [485] 1.3 The maximum thickness of plates furnished under this specification is 4 in. [100 mm] for Class 1 and 6 in. [150 mm] for Class 2 and Class 3. 1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system is to be used independently of the other without combining values in any way. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Sidokset
Velvoittavat viittaukset
Tässä julkaisussa ei ole velvoittavia viittauksia
Tekninen komitea
Vahvistuspäivä
01.03.2019
Julkaisupäivä
01.03.2019
Sivumäärä
3
Julkaisun kieli
englanti

Takaisin